Rizolin Sound Insulation – F



Used for acoustic, vibration insulation of vehicles; in ventilation systems of trading spaces, production facilities, public spaces, communication lines.RIZOLIN Sound Insulation F is a selfadhesive bitumen and polymeric material with additional degree of protection made of aluminium foil. The material is waterproof, resistant to vibrations and mechanical influences, bioresistant.To apply Rizolin Sound Insulation — F it is enough to take off a release film, press the material to a dry and degreased surface and roll it down with a roller. Track beds are laid in seams, with the bitumen and polymeric side to the base. ATTENTION Selfadhesive material properties retain at an air temperature above +10°С. If faulty adhesion has occurred, the material can be heated from adhesive side till appearance of high luster.

Films and sheets, plastic
  • Foil Surfaced
  • Adhesive Polymeric
  • Rolled Waterproofing

Product features

Thickness, mm 2. ± 0,15
Breaking force under tension in longitudinal/transverse directions, not less 800/900
from steel surface 1,5
from concrete surface 1,0
from wooden surface 0,5
Thermal resistance within 2 hours in the upright position, °С, not less +70 ÷ +80
Radius of curvature temperature (25±2) mm, °С, not above -25
Water absorption, %, not more 1
Self-adhesive properties of the material, not less, °С +15
Operating temperature, °С -50 ÷ +50
Dynamic modulus of elasticity under 2 kPa, MPa not above 0,5
Level recession index of impact sound ḺP dB, not less 20
Thermal conductivity, not above, W/m deg 0,037
Waterproofing under a pressure not less than 0,01 kgf/ cm2 within not less than 72 hours absolute
Waterproofing under a pressure not less than 0,5 MPa within 10 min. water-resisting
Reinforcing base Fiberglass cloth
Upper layer Aluminum foil (30 um)
Lower layer Release film
Roll weight, kg 20
Length/width, m 10x1
Manufacturers’ packaging Orange polyethylene with corporate logo